Performance evaluation of different materials as chills in sand casting of aluminium alloy.

Thesis Overview

<p> </p><div><p><strong>1.0</strong>&nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp;<strong>INTRODUCTION</strong><br><strong>1.1 Background to the study</strong><br>&nbsp;<br>Metal casting is a shape forming process whereby molten metal is poured into a prepared mould and allowed to solidify such that the shape of the solidified object is determined by the shape of the mould cavity. Sand casting is a metal casting process characterized by using sand as the mould material (Ibhadode, 2001). Casting can be broadly divided into two main categories as expendable and nonexpendable mould casting. It can also be classified according to the mould material used to cast the metal such as sand casting, ceramic casting or metal mould casting and depending on the pouring methods as gravity casting, low pressure die casting and high pressure die casting (Navaneeth, 2009).<br>Good mechanical properties are achieved in sand casting with the help of metallic insert in the mould known as chill (Mehr, 2012). Strong directional solidification is difficult to obtain in casting of intricate part made of aluminum alloys without the use of chills. The tendency for solidification to start throughout the metal makes proper feeding difficult. Chills must often be used to obtain satisfactory directional solidification (Chi-Yuan <em>et al.,</em>&nbsp;2006).<br>Chills are metallic inserts moulded into the sand surface to promote high solidification rate in metal casting. Normally the metal in the mould cools at a certain rate relative to thickness of the casting. When the geometry of the moulding cavity prevents directional solidification from occurring naturally, a chill can be strategically placed to help promote it to obtain good mechanical properties. Chills are of two types, internal and external chills.</p><p></p></div><h3></h3><br> <br><p></p>