Effect of eggshell as a filler on the mechanical properties of flexible polyurethane foam
Table Of Contents
Project Abstract
Traditionally, calcium carbonate is used as a filler in foam industries and studies have shown that egg-shell contains about 94 % calcium carbonate. The effect of egg-shell in flexible polyurethane foam was studied in this work. Foam with no filler was produced as a control. The egg-shell was beneficiated, characterized and used as filler in flexible polyurethane foam production with varying loads from 5w% to 15 w% at 2.5 w% interval. The effect of various particle sizes on the egg-shell was also studied. Conventional calcium carbonate was also used and the result compared against the produced egg-shell filled foam samples. The produced samples were characterized for compression set, indentation hardness, elongation at break, tensile strength, heat ageing elongation and tensile strength, support factor and density. Scanning electron microscopy (SEM) was also used to study the foamâs morphology. The result of beneficiation showed that the amount of CaCO3 increased by 1.355 % after beneficiating the egg-shell. The results indicated that 45 µm particle size egg-shell was better in most of the properties than other particle sizes tested, with values closest to the control. The highest elongation, tensile strength before and after heat ageing were obtained at 5 wt% of egg-shell. The results also showed that the egg-shell filled foams at 63 µm particle size and 5 wt% loading for tensile strength and elongation before and after heat ageing tests were higher than calcium carbonate filled foam by 1.04 %, 2.66 kN/m2, 0.82 % and 2.22 kN/m2, respectively. In all cases, the density increase with increase in filler loading and particle size. The SEM analysis showed that cell openings of the produced filled foams decreased as particle size and filler content were increased.
Project Overview
1.0 INTRODUCTION
A brief review of the research work is given in this chapter.
1.1 Background of the Study
Solid foam is formed when gas is blown through solidifying plastic. Depending on its ability to retain original shape after compression, it can be classified as either flexible or rigid, Isa et al.,(2012). The foam can either be closed or open cell foams. In closed cell foams, the foam cellsare isolated from each other while the open cell foams are made up of broken cell walls, Babalola and Dominic, (2012).
Flexible polyurethane (PU) foam is one of the major productions from urethane material. Flexible polyurethane foams are used as cushioning material for automotive seat, mattress, furniture, and in packaging etc. According to Klempner and Sendijarevic (2004), flexible polyurethane material has become such widely usedbecause of its excellent light weight, strength to weight ratio performance and the most important is, it offers degree of comfort, protection and utility not matched by other single materials. This usefulness prompts the increase in the prices of polyurethane products consistently over the years which in turn necessitated the incorporation of variety of fillers into foam samples.
Also, the prices of flexible polyurethane foams are becoming increasingly high due to the high cost of raw materials (Onuegbuet al., 2010). The raw materials are mostly liquid reagents and chemicals obtained from petrochemicals and agro-products. The raw materials needed for the production of flexible polyether foam include polyol poly isocyanate, blowing agents, catalysts surfactants and additive such as fillers (Onuegbuet al., 2005).
Blazingprojects Mobile App
📚 Over 50,000 Project Materials
📱 100% Offline: No internet needed
📝 Over 98 Departments
🔍 Software coding and Machine construction
🎓 Postgraduate/Undergraduate Research works
📥 Instant Whatsapp/Email Delivery
Related Research
Design and Optimization of a Chemical Process for Sustainable Production of Biofuels...
The project "Design and Optimization of a Chemical Process for Sustainable Production of Biofuels" focuses on developing an efficient and environmenta...
Optimization of Biofuel Production from Algae...
The project on "Optimization of Biofuel Production from Algae" focuses on exploring innovative strategies to maximize the efficiency of biofuel produc...
Design and Optimization of a Novel Chemical Process for Sustainable Energy Productio...
The project topic "Design and Optimization of a Novel Chemical Process for Sustainable Energy Production" focuses on the development of an innovative ...
Design and Optimization of a Bioreactor for Production of Biofuels...
The project topic "Design and Optimization of a Bioreactor for Production of Biofuels" focuses on the development of an innovative system for the prod...
Optimization of Bioreactor Design for Production of Bioethanol from Agricultural Was...
The project on "Optimization of Bioreactor Design for Production of Bioethanol from Agricultural Waste" aims to address the growing need for sustainab...
Optimization of Biogas Production from Food Waste through Anaerobic Digestion...
The project topic "Optimization of Biogas Production from Food Waste through Anaerobic Digestion" focuses on the sustainable conversion of food waste ...
Optimization of Biodiesel Production Using Microalgae as Feedstock...
The project topic, "Optimization of Biodiesel Production Using Microalgae as Feedstock," focuses on the sustainable production of biodiesel, a renewab...
Optimization of Waste Water Treatment Processes using Advanced Chemical Engineering ...
The project topic "Optimization of Waste Water Treatment Processes using Advanced Chemical Engineering Techniques" focuses on enhancing the efficiency...
Design and Optimization of a Sustainable Process for Bioethanol Production from Agri...
The project topic "Design and Optimization of a Sustainable Process for Bioethanol Production from Agricultural Waste" focuses on the development of a...